Comparative synthesis methods of disordered LiNi0.5O4 spinel as a lithium-ion battery's cathode for high energy desity applications
Loading...
Date
2017
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
Terengganu: Universiti Malaysia Terengganu
Abstract
LiNi0.5Mn1.5O4 has been successfully synthesized by glycine-assisted solution route at low-temperature reaction, ball-milling, and ionic liquid-assisted rheological phase body reaction method, followed by thermal treatments at 750, 850, and 950 °C, respectively for 12 h. The X-ray diffraction patterns of all samples can be assigned to a cubic spinel LiNi0.5Mn1.5O4 with fd3m space group (Joint Committee on Powder Diffraction Standards-card no: 80-2162). From the transmission electron microscope images, the d-spacing between the lattice fringes is approximately 0.47 nm and consistent with the characteristic plane (111) of fd3m for LiNi0.5Mn1.5O4. For LiNi0.5Mn1.5O4 synthesized via glycine-assisted solution route at low-temperature reaction, pure phase of LiNi0.5Mn1.5O4 was obtained for sample S750 and S850, while NiO peaks are arises in sample S950.
Description
Keywords
TK 2941 .N8 2017, Nur Diyana Rosedhi, Storage batteries - Lithium ion batteries